In daily plate production, the processing methods required for different plate structures are also different. Generally, the production of particleboard is mainly based on veneer. The use of veneer technology in the processing process is very important. The relevant details are We must understand clearly to ensure that the performance of the finished veneer of the particle board factory is excellent, so that it can obtain the corresponding application effect. What should we be clear about?

When veneer the particleboard, the pressure must be moderate, generally 2-3MPa, too low will affect the bonding strength of the substrate and the impregnated paper, and too high will damage the board. The hot pressing time depends on the curing speed of the impregnated resin and the hot pressing temperature, generally 40-50s is appropriate, too long time will cause the resin to be over-cured and lose its due elasticity, causing cracks and cracks in the subsequent processing. Warping, too short a time, insufficient resin curing, easy to produce sticking phenomenon, and affect the performance of the product surface, affect the durability of the product.

The processing base material is also the relevant details that must be clear in the production of particleboard manufacturers. The selected raw materials are required to have a smooth surface, uniform sanding, and a moisture content of 6% to 10%. The high moisture content causes bulging during the veneer process. Foaming, delamination, etc., the low moisture content causes the surface to not be well wetted during hot pressing, resulting in cardboard delamination.